- News
- Books
Featured Books
- pcb007 Magazine
Latest Issues
Current IssueThe Growing Industry
In this issue of PCB007 Magazine, we talk with leading economic experts, advocacy specialists in Washington, D.C., and PCB company leadership to get a well-rounded picture of what’s happening in the industry today. Don’t miss it.
The Sustainability Issue
Sustainability is one of the most widely used terms in business today, especially for electronics and manufacturing but what does it mean to you? We explore the environmental, business, and economic impacts.
The Fabricator’s Guide to IPC APEX EXPO
This issue previews many of the important events taking place at this year's show and highlights some changes and opportunities. So, buckle up. We are counting down to IPC APEX EXPO 2024.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - pcb007 Magazine
Estimated reading time: 1 minute
Contact Columnist Form
Controlling the ENIG Process for Optimum Efficiency and Performance
Introduction
In last month’s Trouble in Your Tank, different levels of corrosion in the nickel deposit were presented. In addition, the suggestion was made that mid-phosphorous content EN process was more beneficial with respect to solderability, as opposed to a high phos content nickel deposit. Certainly, concerns with corrosion of the nickel (with lower phos) were allayed as long as the proper process controls were in place. Ideally, the ENIG process must provide the optimum in solder joint reliability while operating at the highest level of cost efficiency. All too often, process parameters that have the most influence on these critical attributes are poorly understood. An example of poor control is shown in Figure 1. The gold deposit has been removed in order to expose the electroless nickel surface.
It is very difficult to discern any anomalies in the nickel deposit without removing the gold. It is clear from the SEMs in Figure 1 that there is significant corrosion on the electroless nickel surface. Obviously, this is an unacceptable situation, and in order to prevent it one must work harder to optimize and control the electroless nickel-immersion gold process. Some of these factors will now be presented in detail.
Critical Electroless Nickel Features:
- Phosphorous content control in the electroless nickel deposit. Don’t underestimate this important parameter.
- Stabilizers in the EN solution influence phosphorous content in the deposit.
- Phos content has strong influence on solderability, immersion gold deposit thickness and potential for hyper-corrosion.
Let’s look at these points in a little more detail.
As I have written in this monthly column on many occasions, operating the chemical processes within the process window is the key to consistent and predictable performance. After all, your customers should expect no less from you. So with respect to #1 above, it is recommended that the EN process be able to maintain a reasonably tight window with respect to phos content through five metal (MTOs) turnovers in the nickel solution.
Read the full column here.
Editor's Note: This column originally appeared in the August 2014 issue of The PCB Magazine.
More Columns from Trouble in Your Tank
Trouble in Your Tank: Supporting IC Substrates and Advanced Packaging, Part 5Trouble in Your Tank: Electrodeposition of Copper, Part 6
Trouble in Your Tank: Electrolytic Copper Plating, Part 5
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 4
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 3
Trouble in Your Tank: Electrodeposition of Copper, Part 4—Addition Agents
Trouble in Your Tank: Lead-free and the Fabrication Challenge, Part 1
Trouble in Your Tank: Processes to Support IC Substrates and Advanced Packaging, Part 2